The effect of aluminium on twinning in binary alpha-titanium
,
Joao Quinta da Fonseca,
Matthew Thomas,
Shu-Yan Zhang,
Joe Kelleher,
Pascal Manuel,
Michael Preuss
Acta Materialia, Volume: 103, Pages: 341 - 351
Swansea University Author:
Leo Prakash
-
PDF | Version of Record
Released under the terms of a Creative Commons Attribution License (CC-BY).
Download (3.74MB)
DOI (Published version): 10.1016/j.actamat.2015.09.048
Abstract
The deformation mechanisms of binary Ti–Al model alloys (0–13.1 at.% Aluminium) have been investigated with respect to the twinning activity using in-situ loading in combination with neutron diffraction as well as detailed post mortem electron backscatter diffraction analysis. A consistent starting...
| Published in: | Acta Materialia |
|---|---|
| ISSN: | 1359-6454 |
| Published: |
2016
|
| Online Access: |
Check full text
|
| URI: | https://cronfa.swan.ac.uk/Record/cronfa24179 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Abstract: |
The deformation mechanisms of binary Ti–Al model alloys (0–13.1 at.% Aluminium) have been investigated with respect to the twinning activity using in-situ loading in combination with neutron diffraction as well as detailed post mortem electron backscatter diffraction analysis. A consistent starting grain size and texture was generated for all alloys promoting tensile twinning during compression testing. Long-wavelength neutron diffraction and selected area diffraction transmission electron microscopy analysis were carried out to detect evidence of Aluminium ordering and Ti3Al formation.It was found that raising the Aluminium content in Titanium does first slightly enhance twinning, with {10View the MathML source2}<10View the MathML source1> tensile twinning being by far the dominant type, while the critical residual intergranular strains for twin initiation decreases. This suggests that either the lowering of stacking fault energy by Aluminium or its solute solution strengthening effect are important factors. At around 7 at.% Aluminium a turning point in twinning activity was noticed and a further increase in Aluminium did result in a dramatic loss of twinning activity particularly when the material had been exposed to an additional low temperature age. The dramatic decrease of twinning activity is strongly correlated with increasing evidence of short range ordering and also early signs of Ti3Al-formation in case of the highest Aluminium content. In addition, electron backscatter diffraction analysis revealed that the formation of Aluminium ordered zones do severely hinder growth of twin boundaries. |
|---|---|
| Keywords: |
Deformation twinning; Ti–Al binary alloys; Neutron diffraction; EBSD; Short range ordering |